# Influence of annealing on structural and optical properties of n-TiO2 thin films grown by sol-gel spin coating
> Gareso P.L.

URL kanonis: https://discover.unhas.ac.id/publications/influence-of-annealing-on-structural-and-optical-properties-of-n-tio2-thin-films
Jurnal / Konferensi: Journal of Physics Conference Series
Tahun terbit: 2019
DOI: https://doi.org/10.1088/1742-6596/1242/1/012037
ISSN: 17426588
Citations: 1

## Authors
- Gareso P.L.

## Abstract
Abstract The influence of thermal annealing to the properties of n -TiO 2 thin films fabricated by sol-gel spin coating has been investigated using X-ray diffraction (X-RD) and UV-Vis optical transmittance measurements. TiO 2 thin films were prepared by dissolving TiO 2 Nano-powders into a solvent of ethanol and it becomes sol-gel. The sol-gel of TiO 2 was deposited on indium tin oxide (ITO) substrate. Then, the TiO 2 the thin films were inserted into tube furnace for annealing in the temperature range of 300 0 C to 500 0 C during 60 minutes. Based on the xray diffraction results, the crystal structure of TiO 2 is anatase phase structures. The crystalline size of TiO 2 films after annealing at 300°C was 46.6 nm and it slightly decreased to 46.2 nm after annealing at 500°C. The optical transmittance value of TiO 2 film increased after annealing in comparison before annealing the TiO 2 film.

## Keywords
- Materials science
- Sol-gel
- Annealing (glass)
- Spin coating
- Anatase
- Thin film
- Chemical engineering
- Transmittance
- Analytical Chemistry (journal)
- Nanotechnology
- Composite material
- Optoelectronics
- Photocatalysis
- Chromatography
- Chemistry
- Organic chemistry
- Engineering
- Catalysis

---
Sumber: Discover Unhas — RIMS Universitas Hasanuddin.
Saat mengutip, gunakan DOI bila tersedia atau URL kanonis di atas.