# Compressive Strength of Zeolite-Based Geopolymer Paste
> Djamaluddin A.R.

URL kanonis: https://discover.unhas.ac.id/publications/compressive-strength-of-zeolite-based-geopolymer-paste
Jurnal / Konferensi: Aip Conference Proceedings
Tahun terbit: 2022
DOI: https://doi.org/10.1063/5.0094926
ISSN: 0094243X
Citations: 2

## Authors
- Djamaluddin A.R.

## Abstract
This paper presents the compressive strength of zeolite-based geopolymer paste produced with various alkali to zeolite (A/Z) ratio of 0.4-0.7; and curing temperature (60°C and 80°C for 24 h) with sodium hydroxide (Na0H) molarity of 8 M. Specimens were tested for compressive strength after 28 days in ambient temperature. The test results showed that A/Z and curing temperature significantly influenced the compressive strength values. The optimum compressive strength was achieved with A/Z ratio of 0.5 and cured at 60° which is about 18.34 MPa. The zeolite-based geopolymer paste prepare in this study can be used for structural components from compressive strength viewpoint.

## Keywords
- Geopolymer
- Compressive strength
- Curing (chemistry)
- Materials science
- Zeolite
- Composite material
- Sodium hydroxide
- Molar concentration
- Chemical engineering
- Chemistry
- Catalysis
- Organic chemistry
- Engineering

---